MIL積層セラミックチップコンデンサMLCC CCAE
媒体はクラスIセラミックです, 良好な周波数特性と高い静電容量の安定性を備えています;
cords製品の各バッチが受ける 100% 温度ショックスクリーニングと高温電気荷重スクリーニング;
s共鳴回路に適しています, カップリング回路, and circuits that require low loss, 高い静電容量安定性, and high insulation resistance in various military electronic devices.
Ordering Example
CCAE 0805 CG 101 J 1NS と | J | ||||||
シリーズ |
External
dimensions |
温度
coefficient |
キャパシタンス |
許容範囲 |
定格
電圧 |
ターミナル
electrode |
Quality Grade |
SMD MLCC |
According to the table below |
CG:0±30ppm/℃ CH:0±60ppm/℃ -55~+125℃ |
Numerical method, 101 is 100pF |
According to the table below |
standard method 50V |
Basic metallization
– metal shielding layer – tin (tin/lead alloy containing at least 3% 鉛) |
According to the table below |
- Comparison Table of Quality Levels and Execution Standard
-
Quality Grade
Quality grade code
Implement detailed specifications
Refer to the general standard for execution
Seven specialties plus
G+
QJ/PWV411-2012
QZJ840624 Ceramic Capacitor “Seven Specialized” Technical Conditions Seven specialties
G
QJ/PWV415-2012
QZJ840624 Ceramic Capacitor “Seven Specialized” Technical Conditions Military screening S QJ/PWV401-2010 GJB192A-1998 General military J QJ/PWV419-2012 GJB192A-1998
Temperature coefficient code | Nominal temperature coefficient | Working temperature range |
CG | 0±30 ppm/℃ | -55℃〜+ 125℃ |
CH | 0 ±± 60 ppm/℃ |
サイズコード |
Dimensions mm | ||||
L | W | Tmax | ![]() |
||
0402 | 1.00±0.15 | 0.50±0.05 | 0.55 | ||
0603 | 1.60±0.15 | 0.80±0.15 | 0.95 | ||
0805 | 2.00±0.20 | 1.25±0.20 | 1.40 | ||
1206 | 3.20±0.20 | 1.60±0.20 | 1.90 | ||
1210 | 3.20±0.40 | 2.50±0.30 | 2.80 | ||
1812 | 4.50±0.50 | 3.20±0.40 | 3.50 | ||
2220 | 5.70±0.50 | 5.00±0.50 | 5.20 | ||
2225 | 5.70±0.50 | 6.30±0.50 | 6.20 |
Temperature coefficient code | Nominal temperature coefficient | Working temperature range |
CG | 0±30 ppm/℃ | -55℃〜+ 125℃ |
CH | 0 ±± 60 ppm/℃ |
Temperature coefficient
Temperature coefficient code | Nominal temperature coefficient | Working temperature range |
CG | 0±30 ppm/℃ | -55℃〜+ 125℃ |
CH | 0 ±± 60 ppm/℃ |
- Allowabledeviationof capacitance
公称静電容量範囲 | Allowable deviation range | コード |
0.1 pF~0.9 pF | ±0.10pF、±0.25pF、±0.50pF | NS、C、D |
1.0 pF~8.2 pF |
±0.10pF、±0.25Pf
±0.50pF、±1% |
NS、C、D、F |
CR≥10pF |
±1% / ±2% | F/G |
±5% | J | |
±10% | K |
アイテム | Test conditions | performance index |
Capacity CR | Test frequency: CR ≤1000pF, 1MHz ± 10%;
CR > 1000pF, 1KHz ± 10% Test voltage:1.0V ± 0.2Vrms |
When CR ≥ 50pF, tg δ≤ 15×10−4
When CR < 50pF, tg δ≤1.5x(150/CR+7)x10−4 |
Tangent of the loss Angle Tg δ | ||
Insulation resistance IR |
Test voltage: rated voltage UR; テスト時間: 1min±5s | IR ≥ 1×105 MΩ or 1000 · μ F,
いずれか小さい方 |
Voltage endurance | Test voltage: 2.5あなたは; テスト時間: 5s±1s | No breakdown, arcing or visible damage |
前書き
誘電体の種類とコンデンサ
◆高周波タイプ: この種の誘電材料のコンデンサは、クラスⅠコンデンサと見なされます,
高周波COGを含む、COHコンデンサとHGなどの温度補償コンデンサ, LG, PH,
RH,SH, TH, 新着, SL. COGの電気的特性、COHコンデンサは最も安定したコンデンサであり、常に変化します
温度付き, 電圧と時間. 低損失と高安定性が要求されるアプリケーションに適しています,
HG,LG,PH,RH,SH,TH,新着,SLコンデンサの静電容量は温度によって変化します。これらはアプリケーションに適しています
ここで、低損失および温度補償回路.
◆X7R、X5R、X7S、X6S:X7R、X5R、X7S、X6S材料は、誘電率が高い材料の一種です. コンデンサ
この種類の材料で作られたクラスIIコンデンサと見なされる静電容量はクラスthatよりも高い.
これらのコンデンサは、半安定した温度特性を持つものとして分類され、幅広い温度で使用されます
範囲, これらの種類の回路では, DCブロッキング, デカップリング, バイパス, 周波数識別など.
◆Y5V:この種類の材料で作られたコンデンサは、すべてのセラミックコンデンサの中で最も高い誘電率です. 彼らです
中程度の温度範囲で使用され、不安定なために高容量が必要なアプリケーション
温度係数, ただし、適度な損失と容量の変化は許容できる場合. その静電容量と
散逸率は測定条件に敏感です, 温度や電圧など, 等.
◆Z5U:この種の材料で作られたコンデンサは、クラスIIコンデンサと見なされます, その温度特性
X7RとY5Vの間. この種のコンデンサの静電容量は不安定であり、温度や温度に敏感です
電圧. 室温に近い環境で低 DC バイアスで動作するアプリケーション回路のバイパスおよびデカップリングに最適.