MIL RF マイクロ波積層セラミックチップコンデンサ MLCC CCDA
●It has the characteristics of low loss, high electrical capacity stability and high reliability;
● Suitable for all kinds of equipment in the high frequency circuit, amplification circuit
Temperature coefficient: NPO: 0 ± 30ppm /℃
Capacitance drift: no more than ± 2% or ± 0.05 pF, take the larger
Loss angle tangent: not exceeding 15% at a frequency of 1 MHz / 1 キロヘルツ
絶縁抵抗 (25℃): 100000M Ω
Medium voltage resistance (test surge current does not exceed 50mA): 5 あなたは
動作温度: -55〜125℃
divide into groups | inspecting item | Requires the chapter number | Test method chapter number | sampling plan |
A divide into groups | Voltage treatment | 3.8 in ZZR-Q / CT 20003-2018 | 4.5.3 in GJB 192B- 2011 | 100% |
A divide into groups |
絶縁抵抗 (125℃) |
3.11 in ZZR-Q / CT 20003- 2018 |
4.5.6 in GJB 192B- 2011 |
In accordance with GJB 192B-2011
テーブル 6 |
A divide into groups |
Visual and mechanical inspection | 3.3 in ZZR-Q / CT 20003- 2018,
.4.1 3,3.28 ,3.29 |
4.5.2 in GJB 192B- 2011 |
In accordance with GJB 192B-2011
テーブル 6 |
A divide into groups | solder ability | 3.15 in ZZR-Q / CT 20003- 2018 | 4.4.2 in GJB 192B- 2011 | 13 samples, そして 0 failed |
前書き
誘電体の種類とコンデンサ
◆高周波タイプ: この種の誘電材料のコンデンサは、クラスⅠコンデンサと見なされます,
高周波COGを含む、COHコンデンサとHGなどの温度補償コンデンサ, LG, PH,
RH,SH, TH, 新着, SL. COGの電気的特性、COHコンデンサは最も安定したコンデンサであり、常に変化します
温度付き, 電圧と時間. 低損失と高安定性が要求されるアプリケーションに適しています,
HG,LG,PH,RH,SH,TH,新着,SLコンデンサの静電容量は温度によって変化します。これらはアプリケーションに適しています
ここで、低損失および温度補償回路.
◆X7R、X5R、X7S、X6S:X7R、X5R、X7S、X6S材料は、誘電率が高い材料の一種です. コンデンサ
この種類の材料で作られたクラスIIコンデンサと見なされる静電容量はクラスthatよりも高い.
これらのコンデンサは、半安定した温度特性を持つものとして分類され、幅広い温度で使用されます
範囲, これらの種類の回路では, DCブロッキング, デカップリング, バイパス, 周波数識別など.
◆Y5V:この種類の材料で作られたコンデンサは、すべてのセラミックコンデンサの中で最も高い誘電率です. 彼らです
中程度の温度範囲で使用され、不安定なために高容量が必要なアプリケーション
温度係数, ただし、適度な損失と容量の変化は許容できる場合. その静電容量と
散逸率は測定条件に敏感です, 温度や電圧など, 等.
◆Z5U:この種の材料で作られたコンデンサは、クラスIIコンデンサと見なされます, その温度特性
X7RとY5Vの間. この種のコンデンサの静電容量は不安定であり、温度や温度に敏感です
電圧. 室温に近い環境で低 DC バイアスで動作するアプリケーション回路のバイパスおよびデカップリングに最適.