Kapasitor keramik keramik keselamatan SMD-MLCC-CCAC CCAD
The green type capacitors in CCAC/CCAD series are manufactured by using environmentally friendly materials without lead or cadmium.
The terminations are composed of plated nickel and pure tin to feature the superior leaching resistance during soldering.
NOMOR BAGIAN
| CCAC | 1808 | B | 102 | K | 3H | T | F | Q |
| JINPEI
Seri |
Ukuran | Dielektrik | Kapasitansi | Toleransi | Impulse Voltage | Kemasan | Ketebalan | Customer Code |
| Meja 1 | Meja 2 | Meja 3 | Meja 4 | Meja 5 | Meja 6 | Meja 7 | Meja 8 | Meja 9 |
| Meja 1 | PDC Family |
| Kode | Keterangan |
| CCAC | Safety X1 & Y2 |
| CCAD | Safety X2 |
| Meja 2 | Ukuran | |||||
| Kode | Keterangan | Kode | Keterangan | Kode | Keterangan | |
| 06 | 1206 (3216) | 12 | 1812 (4532) | 20 | 2220 (5750) | |
| 08 | 1808 (4520) | 21 | 2211 (5728) | |||
| Meja 3 | Karakteristik Bahan Dielektrik | |||
| Kode | Keterangan | Kode | Keterangan | |
| N | NPO/C0G | B | X7R | |
| Meja 4 | Kode Aturan Kapasitansi | |||
| Kode | Keterangan | Kode | Keterangan | |
| 0R5 | 0.5PF | 104 | 104=10×104=100nF | |
| Meja 5 | Toleransi | |||||
| Kode | Keterangan | Kode | Keterangan | Kode | Keterangan | |
| D | ±0.50pF | G | ±2% | K | ±10% | |
| F | ±1% | J | ±5% | M | ± 20% | |
| Meja 6 | Impulse Voltage | |||||
| Kode | Keterangan | Kode | Keterangan | Kode | Keterangan | |
|
2E |
2.5KV |
3000V
3kamu |
2.5KV |
3H | 5KV | |
| 3SAYA | 6KV | |||||
| Meja 7 | Jenis Kemasan | |||
| Kode | Keterangan | Kode | Keterangan | |
| B | Dalam jumlah besar | T | Pita Timbul | |
| Meja 8 | Deskripsi Ketebalan | |||||
| Kode | Keterangan | Kode | Keterangan | Kode | Keterangan | |
| C | 1.25±0. 10 mm | E | 1.60±0.20 mm | G | 2.50±0.30 mm | |
| D | 1.40±0. 15 mm | F | 2.00±0.20 mm | H | 2.80±0.30 mm | |
| Meja 9 | Customer Code | |||||
| Kode | Keterangan | Kode | Keterangan | Kode | Keterangan | |
| G | RoHscompliant | Q | Anti-Arcing | E | Anti-Bending | |
| H | Keandalan tinggi | Z | Anti-Arcing+Anti-Bending | |||
GENERAL ELECTRICAL DATA
| Dielektrik | COG | X7R | |
| Ukuran | 1808, 1812, 2211 | 1808, 1812, 2211, 2220 | 1206 |
| Tegangan terukur | 250vaksin | 2.5KVdc | |
|
Kisaran kapasitansi |
X1/Y2 Class (Impulse 6KV) : 4pF ~ 100pF X1/Y2 Class (Impulse 5KV) : 3pF ~ 720pF X2 Class : 3pF ~ 1000pF |
X1/Y2 Class : 100pF ~ 4700pF X2 Class : 100pF ~ 56000pF |
100pF ~ 1000PF |
|
Toleransi kapasitansi |
J (±5%) K (±10%) M (± 20%) |
||
|
Tan δ |
≤2.5% |
||
|
Kapasitansi & Tan δ Test condition |
Measured at the condition of 30~70% related humidity | ||
|
For 25°C at ambient temperature |
Preconditioning for Class II MLCC : Perform a heat treatment at 150±10°C for 1 jam, then leave in ambient condition for 24±2 hours before measurement |
||
|
1.0±0,2Vrms, 1.0KHz±10%, at 25°C ambient temperature |
|||
| Resistensi isolasi | ≥100GΩ or RxC≥1000Ω-F,
mana saja yang lebih kecil |
≥10GΩ or RxC≥500Ω-F,
mana saja yang lebih kecil |
|
| Operating temperature | -55°C hingga +125 °C | ||
| Temperature coefficient | ±30ppm /°C | ±15% | |
| Termination | Cu or Ag/Ni/Sn (lead-free termination) | ||
PERKENALAN
Jenis Bahan Dielektrik dan Kapasitor
◆ JENIS FREKUENSI TINGGI: Kapasitor dari bahan dielektrik semacam ini dianggap sebagai kapasitor KelasⅠ,
termasuk COG frekuensi tinggi、Kapasitor COH dan kapasitor kompensasi suhu seperti HG, LG, PH,
RH,SH, TH, UJ, dialek. Sifat kelistrikan COG、Kapasitor COH adalah yang paling stabil dan selalu berubah
dengan suhu, tegangan dan waktu. Mereka cocok untuk aplikasi yang memerlukan kerugian rendah dan stabilitas tinggi,
HG，LG，PH，RH，SH，TH，UJ，Kapasitor SL berubah seiring suhu sehingga cocok untuk aplikasi
di mana sirkuit kompensasi kerugian rendah dan suhu.
◆ X7R、X5R、X7S、X6S：X7R、X5R、X7S、Material X6S merupakan material yang memiliki konstanta dielektrik yang tinggi. Kapasitor
terbuat dari bahan semacam ini dianggap sebagai kapasitor Kelas Ⅱ yang kapasitansinya lebih tinggi daripada kapasitor kelas Ⅰ.
Kapasitor ini tergolong memiliki karakteristik suhu semi stabil dan digunakan pada suhu yang luas
jangkauan, seperti di sirkuit semacam ini, Pemblokiran DC, decoupling, melewati, pembedaan frekuensi, dll.
◆ Y5V：Kapasitor yang terbuat dari bahan semacam ini memiliki konstanta dielektrik tertinggi dari semua kapasitor keramik. Benar
digunakan pada rentang suhu sedang dalam aplikasi yang memerlukan kapasitansi tinggi karena tidak stabil
koefisien suhu, tetapi kerugian yang moderat dan perubahan kapasitansi dapat ditoleransi. Kapasitansinya dan
faktor disipasi masuk akal untuk mengukur kondisi, seperti suhu dan tegangan, dll..
◆ Z5U：Kapasitor yang terbuat dari bahan semacam ini dianggap sebagai kapasitor KelasⅡ, yang karakteristik suhunya
berada di antara X7R dan Y5V. Kapasitansi kapasitor jenis ini tidak stabil dan peka terhadap suhu dan
voltase. Cocok untuk melewati dan memisahkan sirkuit aplikasi yang beroperasi dengan bias DC rendah di lingkungan yang mendekati suhu kamar.